  • TAGUTI EDM Brass Wire (Most Applicable & High Cost-performance)

    This TAGUTI brass wire draws its properties from high grade alloy. The excellent tensile strength of the wire, as well as the exceptional surface property, improves significantly the cutting precision. It is made by normal brass alloy to be used normal machine condition at WEDM. The auto threading rate can be raised whether the threading mechanism is pipe type, water jet type, or anneal cutting type because the wire is very straight. Also, the surface is treated to prevent brass powdering. This TAGUT wire is suitable in particular for Fanuc, Hitachi, Mitsubishi and Sodick machines. In order to meet the market demands, TAGUTI introduces this brass wire with higher cost-performance.

    Suitable for automatic threading
    Exceptional tensile strength
    Extreme cleanness of the wire
    High reliability during machining
    Obtains excellent surface finish
    Recommended for high precision work

    Brass Wire Variety Characteristics Diameter KG/Roll
    TAGUTI Core Cu Zu35 Ф0.20 5.0KG
    EDM Brass Wire Tensile strength 900N/㎜2 Ф0.25
    (Hard)
    Elongation <3%(Hard)
    Conductibility 20% IACS
    Surface color Golden
     

    Zinc Coated Wire From TAGUTI (Brass Core & Zinc Coating)

    This is a coated TAGUTI brass wire developed in response to a market demand for high quality and precision wire. It is particularly suitable for applications with special requirements for extremely fine precision cuts. The special coating ensures a very clean finish along the cut surfaces as well as a high performance in terms of cutting speed. Compared with brass wire, this TAGUTI type coated wire has faster cutting speed and improves surface roughness and dimension precision. Also, this zinc coated wire guarantees stable conductivity.

    High precision in cutting
    Excellent surface finish – Ra 0.1μm
    Suitable for automatic threading
    Cutting speed up to 20% faster than brass wire
    Uses standard zinc coated technology
    High speed erosion, up to 10% faster than brass wire

    Coated Wire Variety Characteristics Diameter KG/Roll
    AGIE Core CuZu37 Ф0.10 1.6KG
    Cobra CUT A Coating Zu Ф0.15 6.0KG
    Tensile strength 900N/㎜2 Ф0.20 16KG
    (Hard) Ф0.25
    Elongation <2%
    Conductibility 21% IACS
    Surface color Silvery
     

    Coated Wire Variety Characteristics Diameter KG/Roll
    AGIE Core CuZu20 Ф0.25 16KG
    Cobra CUT D Coating CuZu50
    Tensile strength 800N/㎜2
    (Hard)
    Elongation <3%
    Conductibility 29%
    Surface color Brown
     

    Coated Wire Variety Characteristics Diameter KG/Roll
    Charmilles Core CuZu37 Ф0.10 3.7KG
    SWA Coating Zu Ф0.25 15KG
    Tensile strength 900N/㎜2 
    (Hard)
    Elongation <2%
    Conductibility 21%
    Surface color Silvery
     

    Coated Wire Variety Characteristics Diameter KG/Roll
    Charmilles Core Cu Ф0.25 3.7KG
    SWX Coating CuZu50 Ф0.30 8.0KG
    Tensile strength 510N/㎜
    (Half Hard)
    Elongation <8%
    Conductibility 21%
    Surface color Brown
     

  • TAGUTI® MB-9L Mixed bed resin for low-speed wire-cutting

    Product Information:

    TAGUTI MB-9L mixed bed resin dedicated for low speed wire cutting is ready-to-use resin comprised of gel-type strongly acidic cation exchange resin and strongly basic anion exchange resin. It is made with special resin used for high transition and special purification process as well as mixed and compounded according to specific chemical equivalent. MB-9L is appropriate for low speed wire cutting electrical discharge maching, condensate polishing system preparation of high purity water with the major purpose of removing ions and metallic oxides and it is featured by high purity refining, large working exchange capacity and long service life, etc.

    Chemical Structural Formula:

    Basic Characteristics:

    Ionic form H/ OH-
    Functional group Sulfuric acid group/quaternary amine group
    Matrix Crossliked polystyrene
    Structure Gel type
    Appearance Brown yellow, transparent spherical particles

    Physical and Chemical Properties

    Water content           % 52-57
    Particle size range        95% 0.315-1.25
    Uniformity coefficient     1.6
    Bulk density             g/l 700-800
    Wet real density approx    g/ml 1.13
    Transition rate Cation resin H-type transition rate ,   % 99
    Anion resin OH-type transition rate ,  % 90

    Recommended Operating Conditions

    Operating temperature max     60
    Operating flow rate           BV/h 20-90

    Bed depth     600
    Storage temperature   0-40


error: Content is protected !!
link: molybdenum wire | electrolux el500az filter | China Scarf factory | Sunrise | Beston Pump Group | hemocyte analyzer |